Hot-dip galvanized sheet is formed in three steps under high-temperature liquid state:
1. The iron-based surface is dissolved by the zinc solution to form a zinc-iron alloy phase layer;
2. The zinc ions in the alloy layer further diffuse to the matrix to form a zinc-iron miscible layer;
3. The surface of the alloy layer is surrounded by a zinc layer. All employees of the company will make unremitting efforts, tenacious hard work spirit, and on the basis of stabilizing the leading products. Based on the principle of extensive transfer, technology is the market principle. Galvanized sheet factory, galvanized steel sheet, hot-dip galvanized sheet, hot Galvanized sheet, galvanized coil sheet, galvanized iron sheet, high quality galvalumed steel sheet price, deep iron sheet excavation, alliance with the broad masses of people at home and abroad, and seek common development.
What are the disadvantages of hot-dip galvanized steel
Hot-dip galvanized steel has many functions, but also has its disadvantages, mainly: easy to fall off, easy to scratch during construction, galvanized sheet factory, galvanized steel, hot-dip galvanized sheet, hot-dip galvanized sheet, galvanized coil sheet, Galvanized iron sheet, galvanized sheet price, tin sheet zinc particles, air knife streaks, exposed steel, mechanical damage, wave edge, mismatched size, poor steel-based performance, roll printing, etc.
There are many reasons for the galvanized layer to fall off, including surface oxidation, the cold-rolled emulsion is too dirty, the protective gas dew point is too high, galvanized sheet factory, galvanized steel sheet, hot galvanized sheet, hot galvanized sheet, galvanized coil Sheet, galvanized iron sheet, galvanized sheet price, the low hydrogen flow rate of tin metal, and endless evaporation of grease, etc., so you must pay special attention to the integrity of the surface of the galvanized steel sheet when purchasing.